Born2BondTM Flex is a flexible, elastic and low-odor, instant adhesive with exceptional adhesion to a very broad range of materials and surfaces. It has a curing time of only six minutes and becomes a polymer with more than 200% of elongation within 10 minutes. Its working times (in-mixer) can be up to six minutes. It can be used for high-volumetric gap filling, and achieves instant adhesion to most plastics, wood and metals and to porous and irregular surfaces.
FEATURES
- Fixture time in 60 seconds*
- Hardens in 5-10 minutes*
- Elongation > 200 %
- Absorbs impacts and vibrations
- High peel strength
- Bonds a large range of materials** including glass
- Translucent, low blooming
- Gel consistency for precise application
- Non sagging for vertical applications
APPLICATIONS
Typical applications for this product are leather repair, sealing repair, elastic seam sealing, joint sealing, flexible bonding, sealing drafts, flooring and panel bonding, vibration dampening, strengthening parts, glass to rubber bonding for bus and train windows, and luxury clothing.
PRODUCT CHARACTERISTICS
|
Base Technology – Part A/B |
Methoxyethyl cyanoacrylate (A) Plasticizer (B)
|
|
Components 1k – 2k |
2k
|
|
Mix Ratio |
4:1
|
|
Appearance/Color |
Transparent |
|
Gap Filling Capacity |
1 cm (0.39in)
|
|
Temperature Use Range |
-40°C to 60°C (-40°F to 140°F) Open Time |
|
Mixer Life |
6 – 10 mins
|
|
VOC Content – Part A |
61 g/L (ISO 11890-2)
|
|
VOC Content – Part A |
VOC Content – Part A |
|
Base Technology – Part A/B |
Methoxyethyl cyanoacrylate (A) Plasticizer (B)
|
|
Components 1k – 2k |
2k
|
|
Mix Ratio |
4:1
|
|
Appearance/Color |
Transparent |
|
Gap Filling Capacity |
1 cm (0.39in)
|
|
Temperature Use Range |
-40°C to 60°C (-40°F to 140°F) Open Time |
|
Mixer Life |
6 – 10 mins
|
|
VOC Content – Part A |
61 g/L (ISO 11890-2)
|
|
VOC Content – Part A |
VOC Content – Part A |
|
Base Technology – Part A/B |
Methoxyethyl cyanoacrylate (A) Plasticizer (B)
|
|
Components 1k – 2k |
2k
|
|
Mix Ratio |
4:1
|
|
Appearance/Color |
Transparent |
|
Gap Filling Capacity |
1 cm (0.39in)
|
|
Temperature Use Range |
-40°C to 60°C (-40°F to 140°F) Open Time |
|
Mixer Life |
6 – 10 mins
|
|
VOC Content – Part A |
61 g/L (ISO 11890-2)
|
|
VOC Content – Part A |
VOC Content – Part A |
UNCURED PHYSICAL PROPERTIES
|
Viscosity at 25°C (77°F)* – Part A |
120000 – 170000 cP @ 1.5 rpm 6000 – 9000 cP @ 50 rpm
|
|
Viscosity at 25°C (77°F)* – Part B |
70000 – 130000 cP @ 1.5 rpm 3000 – 7000 cP @ 50 rpm
|
|
Specific Gravity |
1.12 g/mL (A) (ASTM D1875: 23°C / 73.4°F) 1.10 g/mL (B) |
|
Refractive Index, ABBE |
1.48 – 1.50
|