Born2BondTM Repair is a patented, gap-filling, instant adhesive and repair product with excellent adhesion to a very broad range of materials and surfaces. Repair is ideal for instant bonding and repairing, because it combines the strength of a structural adhesive with the speed of an instant adhesives. A tough polymer is achieved within a hardening time of under 10 minutes and the gel consistency enables application in any orientation.
FEATURES
- Fixture time in 60 seconds*
- Hardens in 5-10 minutes*
- Instant adhesion with high bonding strength
- Low volume shrinkage : 3 %
- Fills gaps of any volume
- Bonds a large range of materials**
- Machinable once hardened
- Sandable
- Paintable
- Impact resistant
- Gel consistency for precise application
- Non sagging for vertical applications
APPLICATIONS
Typical applications for this product are aftermarket (side mirrors, bumpers, spoiler aprons) repairs, wood repair and reconstruction, rubber door bonding, automotive joint bonding.
PRODUCT CHARACTERISTICS
| Base Technology – Part A/B |
Ethyl Cyanoacrylate (A) Plasticizer (B |
| Components 1k – 2k | 2k |
| Mix Ratio | 4:1 |
| Appearance/Color | Whitish |
| Gap Filling Capacity | Centimeters/Inches |
| Temperature Use Range | -40°C to 80°C (-40°F to 176°F) |
| Open Time | 4 – 10 mins |
| Mixer Life | 5 – 10 mins |
|
VOC Content – Part A |
92 g/L (ISO 11890-2) |
|
VOC Content – Part B |
15 g/L (ISO 11890-2) |
UNCURED PHYSICAL PROPERTIES
|
Viscosity at 25°C (77°F)* – Part A |
120000 – 170000 cP @ 1.5 rpm 6000 – 9000 cP @ 50 rpm |
|
Viscosity at 25°C (77°F)* – Part B |
70000 – 130000 cP @ 1.5 rpm 3000 – 7000 cP @ 50 rpm |
|
Specific Gravity 23°C / 73.4°F) |
1.12 g/mL (A) (ASTM D1875: 1.10 g/mL (B) |
| Refractive Index, ABBE |
Opaque
|
CURED PHYSICAL PROPERTIES
|
Shore Hardness D (ISO 868-2003) |
67 |
|
Soft Point – HDT (ASTM E2092-18a) |
54°C (129.2°F) |
|
Tensile Strength (ISO 527) |
14 MPa |
|
Elastic Modulus (ISO 527) |
1100 MPa |
|
Elongation at Break (ISO 527) |
12% |
|
Glass Transition Temperature |
86°C (186.8°F) |
|
Coefficient of Linear Thermal Expansion (ISO 10545-8) |
58 x 10-6 |
|
Linear Shrinkage (ISO 10563) |
4.3% |
|
Water Absorption (after 24 hrs) (ASTM D-542) |
0.9% |
|
Impact Resistance (after 24 hrs) |
14.7 kJ/m2 |