Born2Bond™ Repair
Born2Bond™ Repair is a patented, gap-filling instant adhesive that combines the speed of a cyanoacrylate with the strength of a structural adhesive. It hardens within 10 minutes into a tough, sandable polymer ideal for bonding a wide variety of materials.
Born2Bond™ Repair Features:
- Fixture time of 60 seconds*
- Fills gaps of any volume
- Hardens in 5–10 minutes*
- Low shrinkage (3%)
- Machinable, sandable, and paintable
- Impact resistant with gel consistency for vertical use
Born2Bond™ Repair Applications:
- Automotive repair (bumpers, mirrors, spoilers)
- Wood reconstruction and bonding
- Rubber bonding and general repairs
About Prostech
Prostech Philippines is a one-stop solution provider for specialty materials and equipment across electronics manufacturing, from PCBA to final assembly. Our core material and equipment solutions include:
- PCB Assembly Materials
- Cleaning & Degreaser
- Circuit Board Protection
- Thermal Management Solutions
- EMI Shielding
- General Assembly Adhesives
- Elastomeric Materials
- Process Equipment: Potting & Coating Systems, UV/ Heat Curing, Plasma Treatment, Tape placement automation, and cleaning machines
Technical Added Value to customer
Prostech offers customized material and process equipment solutions with engineering support throughout R&D, production process optimization, and performance validation. Our in-house lab located in Alabang, Muntinlupa is equipped to conduct electronics material testing, application simulation, and adhesive validation, helping customers reduce the need for onsite trials and accelerate implementation.
International Supply Chain Advantage
Regional warehouse hubs across Vietnam, Singapore, Malaysia, and the Philippines ensure cross-border reliable supply. In Philippines PEZA-bonded warehouse located at Lima Industrial Park, Batangas enables Prostech to provide responsive, demand-based delivery and significantly shortens standard lead time for Philippines customers.
Need help selecting the right product or solution?
PRODUCT CHARACTERISTICS
| Base Technology - Part A/B | Ethyl Cyanoacrylate (A) Plasticizer (B |
| Components 1k - 2k | 2k |
| Mix Ratio | 4:1 |
| Appearance/Color | Whitish |
| Gap Filling Capacity | Centimeters/Inches |
| Temperature Use Range | -40°C to 80°C (-40°F to 176°F) |
| Open Time | 4 - 10 mins |
| Mixer Life | 5 - 10 mins |
VOC Content - Part A | 92 g/L (ISO 11890-2) |
VOC Content - Part B | 15 g/L (ISO 11890-2) |
UNCURED PHYSICAL PROPERTIES
Viscosity at 25°C (77°F)* - Part A | 120000 - 170000 cP @ 1.5 rpm 6000 - 9000 cP @ 50 rpm |
Viscosity at 25°C (77°F)* - Part B | 70000 - 130000 cP @ 1.5 rpm 3000 - 7000 cP @ 50 rpm |
Specific Gravity 23°C / 73.4°F) | 1.12 g/mL (A) (ASTM D1875: 1.10 g/mL (B) |
| Refractive Index, ABBE | Opaque
|
CURED PHYSICAL PROPERTIES
Shore Hardness D (ISO 868-2003) | 67 |
Soft Point - HDT (ASTM E2092-18a) | 54°C (129.2°F) |
Tensile Strength (ISO 527) | 14 MPa |
Elastic Modulus (ISO 527) | 1100 MPa |
Elongation at Break (ISO 527) | 12% |
Glass Transition Temperature | 86°C (186.8°F) |
Coefficient of Linear Thermal Expansion (ISO 10545-8) | 58 x 10-6 |
Linear Shrinkage (ISO 10563) | 4.3% |
Water Absorption (after 24 hrs) (ASTM D-542) | 0.9% |
Impact Resistance (after 24 hrs) | 14.7 kJ/m2 |