Bostik SAF30 120 SA TWO-COMPONENT METHYL METHACRYLATE

  • Product code: SAF30 120 SA
  • Manufacturer: Bostik
  • Package size:
  • Shelf Life: 9 months

Request Quote Request Sample

Designed with patented methyl methacrylate technology, Bostik’s SAF structural  adhesive  product line offers unmatched chemical, environmental, mechanical and fatigue resistance for many industrial applications. Able to bond a wide range of dissimilar substrates, including composites, metals and  plastics, the SAF product line features high elongation from 30-250%, smart viscosity formulation, minimal surface preparation and a wide range of open and curing times.

FEATURES

  • Long open and fixture times, cure time of approximately 120 minutes
  • Non-sag application on vertical surfaces
  •  Excellent environmental resistance

APPLICATIONS

The optimum quality is obtained at room temperature, ideally between 64 – 82°F (18 – 28°C) without post-curing.

Follow the instructions on the product operating guide or contact your Bostik representative for any information concerning product use or dispensing equipment.

RANGE OF APPLICATION

METALS

COMPOSITES

PLASTICS

Steel

Polyester

PVC

Stainless Steel

Vinyl ester

PS

Aluminum

Epoxy

ABS

 

Acrylic (Elium)

PC

 

 

PMMA

 

MECHANICAL PROPERTIES

Properties

Result

Lap shear strength [MPa/ psi]3 thickness 250μm

11 / 1,160

Tensile strength at break [MPa/psi]3

12 – 14 / 1,740 – 2,031

Tensile modulus [MPa/psi]3

800 – 900 / 116,030 – 130,534

Hardness [Shore D]

65 – 70

Elongation at break4

30%

 

 

PRODUCT CHARACTERISTICS

CURING PROPERTIES

Properties

Result

System

Two-component 10:1 volume ratio

Polymerization

Room temperature

 

TYPICAL PHYSICAL PROPERTIES

Properties

Resin

Hardener Bostik SAF D

Appearance

Off-White

White

Density (+/_ 0.02)

1.17

1.16

Viscosity @77°F (23°C)

90,000 – 150,0001

90,000 – 140,0002

Type

Non-sag

 

CURING PROPERTIES

Properties

Result

Open time [min]

80 – 100

Fixture time @77°F (23°C) [min]

105 – 150

Full cure [hours]

24

WEATHERING AND AGING RESISTANCE

Lap shear strength (MPa/psi) with ISO 4587 after D3 cycle. D3 cycle: NF EN ISO 9142, 7 aging cycles (7 days).

LAP SHEAR STRENGTH (MPa/psi)3 THICKNESS 250μm

Substrates

Before aging cycles

After aging cycles D3

Aluminum 6060

11.2 / 1,624 CF

11.5 / 1,668 CF

Stainless steel

7.6 / 1,102 AF

9.8 / 1,421 CF/AF

FPR

8.3 / 1,204 DF

9.0 / 1,305 DF

TDS:Download

Get MSDS

    Please leave your information and we'll get back to you shortly!







    How to bond Hard-to-bond Substrates (Nylon, COC/COP and PEBA) in Medical Devices Assembly? 
    https://prostech.ph/how-to-bond-hard-to-bond-substrates-nylon-coc-cop-and-peba-in-medical-devices-assembly/

    Understanding the Low Surface Energy (LSE) MaterialsNylon in Medical Devices AssemblyCOC/COP (Cyclic Olefin Polymers and Copolymers) in Medical Devices AssemblyBonding
    FIPG & CIPG – A Comprehensive Guide
    https://prostech.ph/fipg-cipg-a-comprehensive-guide/

    1. Overview of Gasket – FIPG and CIPG 2. Key Features and Applications of Each Type1. FIPG – FORMED IN PLACE
    The differences between Silicone-based and Non-silicone Thermal Interface Materials (TIMs)?
    https://prostech.ph/the-differences-between-silicone-based-and-non-silicone-thermal-interface-materials-tims/

    1. Thermal interface materials – TIMs2. Silicone-based or Non-silicone TIMs2.1. Silicone-based thermal interface materials 2.2. Non-silicone thermal interface materials 3. Conclusion In
    tesa® 4928
    https://prostech.ph/tesa-4928/

    tesa® 4928 is a transparent double-sided self-adhesive tape consisting of a PET backing and a modified acrylic adhesive. Features An