HumiSeal 1B58LU is a synthetic rubber conformal coating that air dries and consists of a single component. Its unique chemistry provides it with an exceptional ability to resist moisture vapor permeability and improve thermal stability. The coating is highly flexible, puts low stress on components, can be easily inspected under UV light, and has effortless repairability. Additionally, HumiSeal 1B58LU contains methylcyclohexane, which makes it more environmentally friendly than traditional solvents. It is fully compliant with the RoHS Directive 2002 95 EC and IPC-CC-830.
FEATURES
- a fast drying
- single component
- synthetic rubber
- used with Thinner 903 or 905
HumiSeal 1B58LU conformal coating has
- extremely low moisture vapor permeability
- improved thermal stability
- excellent flexibility, low stress on components
- fluoresces under UV light for ease of inspection and is easily repaired
- methylcyclohexane which is more environmentally friendly than traditional solvents
- full compliance with the RoHS directive 2015/863/EU
- IPC-CC-830 compliant
Product Specification | |
Density, per ASTM D1475 | 0.77 ± 0.02 g/cm3 |
Solids Content, % by weight per Fed-Std-141, Meth. 4044 | 20 ± 1.5 % |
Viscosity, per Fed-Std-141, Meth. 4287 | 240 ± 130 centipoise |
VOC | 628 grams/liter |
Drying Time to Handle per Fed-Std-141, Meth. 4061 | 10 minutes |
Recommended Coating Thickness | 25 – 75 microns |
Recommended Curing Conditions | 24 hrs @ RT or 30 min @ 76°C |
Time Required to Reach Optimum Properties | 7 days |
Recommended Thinner | HumiSeal Thinner 903, 905 |
Recommended Stripper | Stripper 1080 |
Shelf Life at Room Temperature, DOM | 18 months |
Thermal Shock, 50 cycles per MIL-I-46058C | -65°C to 125°C |
Glass Transition Temperature – DSC | -49.6°C |
Tensile Strength, treated at 140°C | 33.6 MPa, 27.0 MPa (after 1,000 hours), 18.6 MPa (after 2,000 hours), 11.6 MPa (after 3,000 hours) |
Extension, treated at 140°C | 503 %, 484 % (after 1,000 hours), 443 % (after 2,000 hours), 96 % (after 3,000 hours) |
Moisture Vapor Transmission, per ASTM E398-03 | 5.2 g/m2 • day • mil |
Dielectric Withstand Voltage, per MIL-I-46058C | >1500 volts |
Insulation Resistance, per MIL-I-46058C | 5.0 x 1014 ohms (500TΩ) |
Moisture Insulation Resistance, per MIL-I-46058C | 7.5 x 1013 ohms (75GΩ) |